硕士邦德UV10LVDC是一个新的组件紫外线和/或加热固化改性环氧树脂高性能粘接树脂，涂料，铸造的应用系统。 当暴露在紫外线光或热的来源，UV10LVDC治愈容易很强的耐化学性债券，涂料或铸件。 治愈UV10LVDC化合物可用于宽的温度范围在-60 ° F至300 ° F。 紫外光固化，最大吸收波长在320-360纳米范围内。 治愈也可以在250 ° F加热约20分钟，在烤箱UV10LVDC复合的影响。 双硕士邦德UV10LVDC治愈能力大大增强UV固化技术的实用程序，扩展其适用性，包括光学透明和不透明组件的组件。 硕士邦德UV10LVDC树脂体系是不是氧抑制，并不需要紫外线或热固化的惰性气氛。 UV10LVDC复合不像大多数其他的UV固化系统，可在第一个广泛治愈厚度可达1 / 4“多，这大大增加了范围UV10LVDC系统的实用性，以铸造和封装，以及粘合和涂层应用。保税集会，涂料和铸件长期耐久性是优秀的，即使暴露在恶劣的环境条件，包括热量，水分，化工，等大师的债券UV10LVDC具有较高的物理强度和优异的耐化学性无机化学品，包括酸，碱和盐以及有机的化学物质，如最常见的溶剂高强度债券获得的金属，陶瓷，玻璃，纸张，许多塑料和弹性体。，复合是100％反应，不含有任何溶剂或稀释剂。固化以最小的影响收缩。硕士邦德UV10LVDC的优越的性能配置文件是由于其独特的化学成分包括一个exceptinally有效的紫外线固化剂和一个优越的热固化催化剂。的快速紫外光固化的机制是由接触市售200瓦的/线性英寸介质压力汞触发蒸汽灯或类似的设备。与此种商业紫外线灯，治疗可以在极短的时间段，如1分钟或在环境温度低影响，当低强度紫外线灯，有些较长的固化时间是必要的。，如前所述，烤箱治愈可以达到大约20分钟。在250 ° F的物理强度，耐化学性和粘接性能完全治愈UV10LVDC化合物的方法由传统的环氧树脂系统展出的。

Master Bond UV10LVDC is a new one component UV and/or heat curable modified epoxy resin system for high performance bonding, coating and casting applications. When exposed to a source of UV light or heat, UV10LVDC cures readily to strong chemically resistant bonds, coatings or castings. The cured UV10LVDC compound can be used over the wide temperature range of -60°F to 300°F. For UV curing, the maximum absorption is found in the 320-360 nanometer range. Cures can also be effected by heating the UV10LVDC compound in an oven at 250°F for approximately 20 minutes. The dual cure capability of the Master Bond UV10LVDC greatly enhances the utility of UV curing technology by extending its applicability to assemblies comprising both optically opaque and transparent components. The Master Bond UV10LVDC resin system is not oxygen inhibited and does not require an inert atmosphere for either UV or thermal cures. Unlike most other UV curing systems, the UV10LVDC compound can be cured in a wide range of section thicknesses up to 1/4″ and more. This greatly increases the range of usefulness of the UV10LVDC system to casting and encapsulation as well as bonding and coating applications. Long term durability of bonded assemblies, coatings and castings is excellent even when exposed to adverse environmental conditions including heat, moisture, chemicals, etc. Master Bond UV10LVDC exhibits high physical strength and superior chemical resistance to inorganic chemicals including acids, bases and salts as well as organic chemicals such as most common solvents. High strength bonds are obtained with metals, ceramics, glass, paper, many plastics and elastomers. The compound is 100% reactive and does not contain any solvents or diluents. Cures are effected with minimal shrinkage. Master Bond UV10LVDC’s superior performance profile is due to its unique chemical composition which includes an exceptinally effective UV curing agent and a superior thermally curing catalyst. The fast UV curing mechanism is triggered by exposure to commercially available 200 watt/linear inch medium pressure mercury vapor lamps or similar equipment. With such commercial UV lamps, cures can be effected in remarkably short time periods, e.g., 1 minute or less at ambient temperatures. When lower intensity UV lamps are employed somewhat longer curing times are necessary. As noted, oven cures can be achieved at 250°F in approximately 20 minutes. The physical strength, chemical resistance and adhesive properties of the fully cured UV10LVDC compound approach those exhibited by conventional epoxy resin systems.

硕士邦德UV10LVDC是一个新的组件紫外线和/或加热固化改性环氧树脂高性能粘接树脂，涂料，铸造的应用系统。 当暴露在紫外线光或热的来源，UV10LVDC治愈容易很强的耐化学性债券，涂料或铸件。 治愈UV10LVDC化合物可用于宽的温度范围在-60 ° F至300 ° F。 紫外光固化，最大吸收波长在320-360纳米范围内。 治愈也可以在250 ° F加热约20分钟，在烤箱UV10LVDC复合的影响。 双硕士邦德UV10LVDC治愈能力大大增强UV固化技术的实用程序，扩展其适用性，包括光学透明和不透明组件的组件。 硕士邦德UV10LVDC树脂体系是不是氧抑制，并不需要紫外线或热固化的惰性气氛。 UV10LVDC复合不像大多数其他的UV固化系统，可在第一个广泛治愈厚度可达1 / 4“多，这大大增加了范围UV10LVDC系统的实用性，以铸造和封装，以及粘合和涂层应用。保税集会，涂料和铸件长期耐久性是优秀的，即使暴露在恶劣的环境条件，包括热量，水分，化工，等大师的债券UV10LVDC具有较高的物理强度和优异的耐化学性无机化学品，包括酸，碱和盐以及有机的化学物质，如最常见的溶剂高强度债券获得的金属，陶瓷，玻璃，纸张，许多塑料和弹性体。，复合是100％反应，不含有任何溶剂或稀释剂。固化以最小的影响收缩。硕士邦德UV10LVDC的优越的性能配置文件是由于其独特的化学成分包括一个exceptinally有效的紫外线固化剂和一个优越的热固化催化剂。的快速紫外光固化的机制是由接触市售200瓦的/线性英寸介质压力汞触发蒸汽灯或类似的设备。与此种商业紫外线灯，治疗可以在极短的时间段，如1分钟或在环境温度低影响，当低强度紫外线灯，有些较长的固化时间是必要的。，如前所述，烤箱治愈可以达到大约20分钟。在250 ° F的物理强度，耐化学性和粘接性能完全治愈UV10LVDC化合物的方法由传统的环氧树脂系统展出的。

Master Bond UV10LVDC is a new one component UV and/or heat curable modified epoxy resin system for high performance bonding, coating and casting applications. When exposed to a source of UV light or heat, UV10LVDC cures readily to strong chemically resistant bonds, coatings or castings. The cured UV10LVDC compound can be used over the wide temperature range of -60°F to 300°F. For UV curing, the maximum absorption is found in the 320-360 nanometer range. Cures can also be effected by heating the UV10LVDC compound in an oven at 250°F for approximately 20 minutes. The dual cure capability of the Master Bond UV10LVDC greatly enhances the utility of UV curing technology by extending its applicability to assemblies comprising both optically opaque and transparent components. The Master Bond UV10LVDC resin system is not oxygen inhibited and does not require an inert atmosphere for either UV or thermal cures. Unlike most other UV curing systems, the UV10LVDC compound can be cured in a wide range of section thicknesses up to 1/4″ and more. This greatly increases the range of usefulness of the UV10LVDC system to casting and encapsulation as well as bonding and coating applications. Long term durability of bonded assemblies, coatings and castings is excellent even when exposed to adverse environmental conditions including heat, moisture, chemicals, etc. Master Bond UV10LVDC exhibits high physical strength and superior chemical resistance to inorganic chemicals including acids, bases and salts as well as organic chemicals such as most common solvents. High strength bonds are obtained with metals, ceramics, glass, paper, many plastics and elastomers. The compound is 100% reactive and does not contain any solvents or diluents. Cures are effected with minimal shrinkage. Master Bond UV10LVDC’s superior performance profile is due to its unique chemical composition which includes an exceptinally effective UV curing agent and a superior thermally curing catalyst. The fast UV curing mechanism is triggered by exposure to commercially available 200 watt/linear inch medium pressure mercury vapor lamps or similar equipment. With such commercial UV lamps, cures can be effected in remarkably short time periods, e.g., 1 minute or less at ambient temperatures. When lower intensity UV lamps are employed somewhat longer curing times are necessary. As noted, oven cures can be achieved at 250°F in approximately 20 minutes. The physical strength, chemical resistance and adhesive properties of the fully cured UV10LVDC compound approach those exhibited by conventional epoxy resin systems.

硕士邦德UV10LVDC是一个新的组件紫外线和/或加热固化改性环氧树脂高性能粘接树脂，涂料，铸造的应用系统。 当暴露在紫外线光或热的来源，UV10LVDC治愈容易很强的耐化学性债券，涂料或铸件。 治愈UV10LVDC化合物可用于宽的温度范围在-60 ° F至300 ° F。 紫外光固化，最大吸收波长在320-360纳米范围内。 治愈也可以在250 ° F加热约20分钟，在烤箱UV10LVDC复合的影响。 双硕士邦德UV10LVDC治愈能力大大增强UV固化技术的实用程序，扩展其适用性，包括光学透明和不透明组件的组件。 硕士邦德UV10LVDC树脂体系是不是氧抑制，并不需要紫外线或热固化的惰性气氛。 UV10LVDC复合不像大多数其他的UV固化系统，可在第一个广泛治愈厚度可达1 / 4“多，这大大增加了范围UV10LVDC系统的实用性，以铸造和封装，以及粘合和涂层应用。保税集会，涂料和铸件长期耐久性是优秀的，即使暴露在恶劣的环境条件，包括热量，水分，化工，等大师的债券UV10LVDC具有较高的物理强度和优异的耐化学性无机化学品，包括酸，碱和盐以及有机的化学物质，如最常见的溶剂高强度债券获得的金属，陶瓷，玻璃，纸张，许多塑料和弹性体。，复合是100％反应，不含有任何溶剂或稀释剂。固化以最小的影响收缩。硕士邦德UV10LVDC的优越的性能配置文件是由于其独特的化学成分包括一个exceptinally有效的紫外线固化剂和一个优越的热固化催化剂。的快速紫外光固化的机制是由接触市售200瓦的/线性英寸介质压力汞触发蒸汽灯或类似的设备。与此种商业紫外线灯，治疗可以在极短的时间段，如1分钟或在环境温度低影响，当低强度紫外线灯，有些较长的固化时间是必要的。，如前所述，烤箱治愈可以达到大约20分钟。在250 ° F的物理强度，耐化学性和粘接性能完全治愈UV10LVDC化合物的方法由传统的环氧树脂系统展出的。

Master Bond UV10LVDC is a new one component UV and/or heat curable modified epoxy resin system for high performance bonding, coating and casting applications. When exposed to a source of UV light or heat, UV10LVDC cures readily to strong chemically resistant bonds, coatings or castings. The cured UV10LVDC compound can be used over the wide temperature range of -60°F to 300°F. For UV curing, the maximum absorption is found in the 320-360 nanometer range. Cures can also be effected by heating the UV10LVDC compound in an oven at 250°F for approximately 20 minutes. The dual cure capability of the Master Bond UV10LVDC greatly enhances the utility of UV curing technology by extending its applicability to assemblies comprising both optically opaque and transparent components. The Master Bond UV10LVDC resin system is not oxygen inhibited and does not require an inert atmosphere for either UV or thermal cures. Unlike most other UV curing systems, the UV10LVDC compound can be cured in a wide range of section thicknesses up to 1/4″ and more. This greatly increases the range of usefulness of the UV10LVDC system to casting and encapsulation as well as bonding and coating applications. Long term durability of bonded assemblies, coatings and castings is excellent even when exposed to adverse environmental conditions including heat, moisture, chemicals, etc. Master Bond UV10LVDC exhibits high physical strength and superior chemical resistance to inorganic chemicals including acids, bases and salts as well as organic chemicals such as most common solvents. High strength bonds are obtained with metals, ceramics, glass, paper, many plastics and elastomers. The compound is 100% reactive and does not contain any solvents or diluents. Cures are effected with minimal shrinkage. Master Bond UV10LVDC’s superior performance profile is due to its unique chemical composition which includes an exceptinally effective UV curing agent and a superior thermally curing catalyst. The fast UV curing mechanism is triggered by exposure to commercially available 200 watt/linear inch medium pressure mercury vapor lamps or similar equipment. With such commercial UV lamps, cures can be effected in remarkably short time periods, e.g., 1 minute or less at ambient temperatures. When lower intensity UV lamps are employed somewhat longer curing times are necessary. As noted, oven cures can be achieved at 250°F in approximately 20 minutes. The physical strength, chemical resistance and adhesive properties of the fully cured UV10LVDC compound approach those exhibited by conventional epoxy resin systems.