硕士邦德UV10FL – 1和UV10FLTK – 1是一种单组分紫外光固化改性剂，可以使用了作为提供高性能铸造和焊接应用。 UV10FL – 1是一种在常温下低粘度液体和UV10FLTK – 1是一种在常温下中等粘度液体。 当暴露在紫外线光源，这些化合物形成强大以及优良的耐化学性化合物在很宽的温度范围内（在320-360 millimicrons最大紫外吸收）使用。 铸件可达1 / 4“厚也有所准备。UV10FL – 1表现出较高的拉伸强度和刚度相比，有些更灵活UV10FLTK – 1。硕士邦德UV10FL – 1和UV10FLTK – 1是不是氧抑制andtherefore不需要用于治疗惰性气体，这些化合物不需要完全由紫外光源作为聚合固化后会继续曝光。不像其他UV系统UV10FL – 1和UV10FLTK – 1化​​合物可在大范围的部分固化厚度高债券优势得到与金属，陶瓷，玻璃，造纸，许多塑料和弹性体，长的粘接强度的耐久性非常好，即使暴露在包括热和潮湿的不利环境条​​件的硕士邦德UV10FL – 1优越的性能配置和UV10FLTK – 1化​​合物由于其独特的化学成分。硕士邦德UV10FL和UV10FLTK是基于一个特别改装的聚合物系统，并包含一个非常有效的潜在UV固化剂系统，快速固化的机制是任何这样的紫外光源引发的方便作为中压汞蒸气灯，随着商业紫外线灯，治疗已经生效在很短的时间段，如1分钟，在环境温度低，即使低强度紫外光源，专治可在几分钟内获得的，没有溶剂或其他被释放的挥发物在固化过程中，债券的优势等于或超过从传统的室温固化双组份获得的环氧树脂胶粘剂组成。贮存硕士邦德UV10FL – 1和UV10FLTK – 1化​​合物的稳定性超出一般未开封下的储存条件6个月容器。

Master Bond UV10FL-1 and UV10FLTK-1 are a one component UV curable modified compounds, ready for use as supplied, for high performance casting and bonding applications. UV10FL-1 is a low viscosity liquid at room temperature and UV10FLTK-1 is a medium viscosity liquid at room temperature. When exposed to a source of UV light these compounds form strong as well as superior chemical resistance compounds suitable for use over a wide temperature range (maximum UV absorption at 320-360 millimicrons). Castings up to 1/4″ thick can also be prepared. UV10FL-1 exhibits a higher tensile strength and stiffness compared to the somewhat more flexible UV10FLTK-1. Master Bond UV10FL-1 and UV10FLTK-1 are not oxygen inhibited andtherefore do not require an inert atmosphere for cure. These compounds need not be fully cured by the UV source as polymerization will continue after exposure. Unlike other UV systems the UV10FL-1 and UV10FLTK-1 compounds can be cured in a wide range of section thicknesses. High bond strengths are obtained with metals, ceramics, glass, paper, many plastics and elastomers. Long term durability of the bond strengths is excellent even when exposed to adverse environmental conditions including heat and moisture. The superior performance profile of the Master Bond UV10FL-1 and UV10FLTK-1 compounds is due to their unique chemical composition. Master Bond UV10FL and UV10FLTK are based on a specially modified polymeric system and contain an exceptionally effective latent UV curing agent system. The fast curing mechanism is triggered by any convenient source of UV light such as medium pressure mercury vapor lamps. With commercial UV lamps, cures have been effected in very short time periods, e.g., 1 minute and less at ambient temperatures. Even with low intensity UV sources, cures can be obtained in minutes. No solvents or other volatiles are released during the curing process. Bond strengths equal or exceed those obtained from conventional room temperature curing two component epoxy resin adhesive compositions. Storage stability of Master Bond UV10FL-1 and UV10FLTK-1 compound exceeds 6 months under the usual storage conditions in unopened containers.

硕士邦德UV10FL – 1和UV10FLTK – 1是一种单组分紫外光固化改性剂，可以使用了作为提供高性能铸造和焊接应用。 UV10FL – 1是一种在常温下低粘度液体和UV10FLTK – 1是一种在常温下中等粘度液体。 当暴露在紫外线光源，这些化合物形成强大以及优良的耐化学性化合物在很宽的温度范围内（在320-360 millimicrons最大紫外吸收）使用。 铸件可达1 / 4“厚也有所准备。UV10FL – 1表现出较高的拉伸强度和刚度相比，有些更灵活UV10FLTK – 1。硕士邦德UV10FL – 1和UV10FLTK – 1是不是氧抑制andtherefore不需要用于治疗惰性气体，这些化合物不需要完全由紫外光源作为聚合固化后会继续曝光。不像其他UV系统UV10FL – 1和UV10FLTK – 1化​​合物可在大范围的部分固化厚度高债券优势得到与金属，陶瓷，玻璃，造纸，许多塑料和弹性体，长的粘接强度的耐久性非常好，即使暴露在包括热和潮湿的不利环境条​​件的硕士邦德UV10FL – 1优越的性能配置和UV10FLTK – 1化​​合物由于其独特的化学成分。硕士邦德UV10FL和UV10FLTK是基于一个特别改装的聚合物系统，并包含一个非常有效的潜在UV固化剂系统，快速固化的机制是任何这样的紫外光源引发的方便作为中压汞蒸气灯，随着商业紫外线灯，治疗已经生效在很短的时间段，如1分钟，在环境温度低，即使低强度紫外光源，专治可在几分钟内获得的，没有溶剂或其他被释放的挥发物在固化过程中，债券的优势等于或超过从传统的室温固化双组份获得的环氧树脂胶粘剂组成。贮存硕士邦德UV10FL – 1和UV10FLTK – 1化​​合物的稳定性超出一般未开封下的储存条件6个月容器。

Master Bond UV10FL-1 and UV10FLTK-1 are a one component UV curable modified compounds, ready for use as supplied, for high performance casting and bonding applications. UV10FL-1 is a low viscosity liquid at room temperature and UV10FLTK-1 is a medium viscosity liquid at room temperature. When exposed to a source of UV light these compounds form strong as well as superior chemical resistance compounds suitable for use over a wide temperature range (maximum UV absorption at 320-360 millimicrons). Castings up to 1/4″ thick can also be prepared. UV10FL-1 exhibits a higher tensile strength and stiffness compared to the somewhat more flexible UV10FLTK-1. Master Bond UV10FL-1 and UV10FLTK-1 are not oxygen inhibited andtherefore do not require an inert atmosphere for cure. These compounds need not be fully cured by the UV source as polymerization will continue after exposure. Unlike other UV systems the UV10FL-1 and UV10FLTK-1 compounds can be cured in a wide range of section thicknesses. High bond strengths are obtained with metals, ceramics, glass, paper, many plastics and elastomers. Long term durability of the bond strengths is excellent even when exposed to adverse environmental conditions including heat and moisture. The superior performance profile of the Master Bond UV10FL-1 and UV10FLTK-1 compounds is due to their unique chemical composition. Master Bond UV10FL and UV10FLTK are based on a specially modified polymeric system and contain an exceptionally effective latent UV curing agent system. The fast curing mechanism is triggered by any convenient source of UV light such as medium pressure mercury vapor lamps. With commercial UV lamps, cures have been effected in very short time periods, e.g., 1 minute and less at ambient temperatures. Even with low intensity UV sources, cures can be obtained in minutes. No solvents or other volatiles are released during the curing process. Bond strengths equal or exceed those obtained from conventional room temperature curing two component epoxy resin adhesive compositions. Storage stability of Master Bond UV10FL-1 and UV10FLTK-1 compound exceeds 6 months under the usual storage conditions in unopened containers.

硕士邦德UV10FL – 1和UV10FLTK – 1是一种单组分紫外光固化改性剂，可以使用了作为提供高性能铸造和焊接应用。 UV10FL – 1是一种在常温下低粘度液体和UV10FLTK – 1是一种在常温下中等粘度液体。 当暴露在紫外线光源，这些化合物形成强大以及优良的耐化学性化合物在很宽的温度范围内（在320-360 millimicrons最大紫外吸收）使用。 铸件可达1 / 4“厚也有所准备。UV10FL – 1表现出较高的拉伸强度和刚度相比，有些更灵活UV10FLTK – 1。硕士邦德UV10FL – 1和UV10FLTK – 1是不是氧抑制andtherefore不需要用于治疗惰性气体，这些化合物不需要完全由紫外光源作为聚合固化后会继续曝光。不像其他UV系统UV10FL – 1和UV10FLTK – 1化​​合物可在大范围的部分固化厚度高债券优势得到与金属，陶瓷，玻璃，造纸，许多塑料和弹性体，长的粘接强度的耐久性非常好，即使暴露在包括热和潮湿的不利环境条​​件的硕士邦德UV10FL – 1优越的性能配置和UV10FLTK – 1化​​合物由于其独特的化学成分。硕士邦德UV10FL和UV10FLTK是基于一个特别改装的聚合物系统，并包含一个非常有效的潜在UV固化剂系统，快速固化的机制是任何这样的紫外光源引发的方便作为中压汞蒸气灯，随着商业紫外线灯，治疗已经生效在很短的时间段，如1分钟，在环境温度低，即使低强度紫外光源，专治可在几分钟内获得的，没有溶剂或其他被释放的挥发物在固化过程中，债券的优势等于或超过从传统的室温固化双组份获得的环氧树脂胶粘剂组成。贮存硕士邦德UV10FL – 1和UV10FLTK – 1化​​合物的稳定性超出一般未开封下的储存条件6个月容器。

Master Bond UV10FL-1 and UV10FLTK-1 are a one component UV curable modified compounds, ready for use as supplied, for high performance casting and bonding applications. UV10FL-1 is a low viscosity liquid at room temperature and UV10FLTK-1 is a medium viscosity liquid at room temperature. When exposed to a source of UV light these compounds form strong as well as superior chemical resistance compounds suitable for use over a wide temperature range (maximum UV absorption at 320-360 millimicrons). Castings up to 1/4″ thick can also be prepared. UV10FL-1 exhibits a higher tensile strength and stiffness compared to the somewhat more flexible UV10FLTK-1. Master Bond UV10FL-1 and UV10FLTK-1 are not oxygen inhibited andtherefore do not require an inert atmosphere for cure. These compounds need not be fully cured by the UV source as polymerization will continue after exposure. Unlike other UV systems the UV10FL-1 and UV10FLTK-1 compounds can be cured in a wide range of section thicknesses. High bond strengths are obtained with metals, ceramics, glass, paper, many plastics and elastomers. Long term durability of the bond strengths is excellent even when exposed to adverse environmental conditions including heat and moisture. The superior performance profile of the Master Bond UV10FL-1 and UV10FLTK-1 compounds is due to their unique chemical composition. Master Bond UV10FL and UV10FLTK are based on a specially modified polymeric system and contain an exceptionally effective latent UV curing agent system. The fast curing mechanism is triggered by any convenient source of UV light such as medium pressure mercury vapor lamps. With commercial UV lamps, cures have been effected in very short time periods, e.g., 1 minute and less at ambient temperatures. Even with low intensity UV sources, cures can be obtained in minutes. No solvents or other volatiles are released during the curing process. Bond strengths equal or exceed those obtained from conventional room temperature curing two component epoxy resin adhesive compositions. Storage stability of Master Bond UV10FL-1 and UV10FLTK-1 compound exceeds 6 months under the usual storage conditions in unopened containers.