硕士邦德聚合物系统LTX 128是一种新开发的高性能快干水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优良的粘接性能，以及非常高的热水浸泡阻力。 这种低VOC C1.3％）聚合物组成配为驼色了38％的固体含量和pH值8.0乳白色液体。 它具有清热密封低至活化温度225 ° F（107 ° C）。 黏附型聚合物为乙烯，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等这些不同的衬底突出。 硕士邦德聚合物系统LTX128已赫然高，如一个2400磅为230磅模量拉伸强度和伸长率超过620％的物理强度性能。 这种独特的粘合剂复合典型属性总结如下。 一个特殊的交联剂称为CRA 128是适合应用在长期耐水性也得到最大限度的发挥提供。 另外一个建议是2％的基础上，乳胶重量。 全粘接强度性能的开发后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128是一种新开发的高性能快干水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优良的粘接性能，以及非常高的热水浸泡阻力。 这种低VOC C1.3％）聚合物组成配为驼色了38％的固体含量和pH值8.0乳白色液体。 它具有清热密封低至活化温度225 ° F（107 ° C）。 黏附型聚合物为乙烯，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等这些不同的衬底突出。 硕士邦德聚合物系统LTX128已赫然高，如一个2400磅为230磅模量拉伸强度和伸长率超过620％的物理强度性能。 这种独特的粘合剂复合典型属性总结如下。 一个特殊的交联剂称为CRA 128是适合应用在长期耐水性也得到最大限度的发挥提供。 另外一个建议是2％的基础上，乳胶重量。 全粘接强度性能的开发后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128是一种新开发的高性能快干水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优良的粘接性能，以及非常高的热水浸泡阻力。 这种低VOC C1.3％）聚合物组成配为驼色了38％的固体含量和pH值8.0乳白色液体。 它具有清热密封低至活化温度225 ° F（107 ° C）。 黏附型聚合物为乙烯，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等这些不同的衬底突出。 硕士邦德聚合物系统LTX128已赫然高，如一个2400磅为230磅模量拉伸强度和伸长率超过620％的物理强度性能。 这种独特的粘合剂复合典型属性总结如下。 一个特殊的交联剂称为CRA 128是适合应用在长期耐水性也得到最大限度的发挥提供。 另外一个建议是2％的基础上，乳胶重量。 全粘接强度性能的开发后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128是一种新开发的高性能快干水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优良的粘接性能，以及非常高的热水浸泡阻力。 这种低VOC C1.3％）聚合物组成配为驼色了38％的固体含量和pH值8.0乳白色液体。 它具有清热密封低至活化温度225 ° F（107 ° C）。 黏附型聚合物为乙烯，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等这些不同的衬底突出。 硕士邦德聚合物系统LTX128已赫然高，如一个2400磅为230磅模量拉伸强度和伸长率超过620％的物理强度性能。 这种独特的粘合剂复合典型属性总结如下。 一个特殊的交联剂称为CRA 128是适合应用在长期耐水性也得到最大限度的发挥提供。 另外一个建议是2％的基础上，乳胶重量。 全粘接强度性能的开发后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.