硕士邦德聚合物系统LTX 128快干新开发的高性能水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优异的粘接性能，以及非常高的热水中浸泡阻力。 这种低VOC C1.3％）聚合物组成，布置为浅黄褐色，38％的固体含量和pH值8.0的乳白色液体。 它具有热封活化温度低为225 ° F（107 ° C）。 乙烯型聚合物，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等等不同基材的附着力是优秀的。 硕士邦德聚合物系统LTX128令人印象深刻的，如一个2400磅230磅的弹性模量，拉伸强度和伸长率超过620％的高物理强度性能。 这种独特的粘合剂化合物的典型特性总结如下。 一个特殊的交联剂称为CRA 128可用于应用程序的长期耐水性得到最大限度的发挥。 建议增加2％的基础上乳胶的重量。 全粘接强度属性后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128快干新开发的高性能水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优异的粘接性能，以及非常高的热水中浸泡阻力。 这种低VOC C1.3％）聚合物组成，布置为浅黄褐色，38％的固体含量和pH值8.0的乳白色液体。 它具有热封活化温度低为225 ° F（107 ° C）。 乙烯型聚合物，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等等不同基材的附着力是优秀的。 硕士邦德聚合物系统LTX128令人印象深刻的，如一个2400磅230磅的弹性模量，拉伸强度和伸长率超过620％的高物理强度性能。 这种独特的粘合剂化合物的典型特性总结如下。 一个特殊的交联剂称为CRA 128可用于应用程序的长期耐水性得到最大限度的发挥。 建议增加2％的基础上乳胶的重量。 全粘接强度属性后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128快干新开发的高性能水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优异的粘接性能，以及非常高的热水中浸泡阻力。 这种低VOC C1.3％）聚合物组成，布置为浅黄褐色，38％的固体含量和pH值8.0的乳白色液体。 它具有热封活化温度低为225 ° F（107 ° C）。 乙烯型聚合物，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等等不同基材的附着力是优秀的。 硕士邦德聚合物系统LTX128令人印象深刻的，如一个2400磅230磅的弹性模量，拉伸强度和伸长率超过620％的高物理强度性能。 这种独特的粘合剂化合物的典型特性总结如下。 一个特殊的交联剂称为CRA 128可用于应用程序的长期耐水性得到最大限度的发挥。 建议增加2％的基础上乳胶的重量。 全粘接强度属性后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.

硕士邦德聚合物系统LTX 128快干新开发的高性能水性脂肪族聚酯聚氨酯复膜胶具有低活化温度和优异的粘接性能，以及非常高的热水中浸泡阻力。 这种低VOC C1.3％）聚合物组成，布置为浅黄褐色，38％的固体含量和pH值8.0的乳白色液体。 它具有热封活化温度低为225 ° F（107 ° C）。 乙烯型聚合物，聚酯，聚氨酯，低密度聚乙烯以及ABS和铝箔等等不同基材的附着力是优秀的。 硕士邦德聚合物系统LTX128令人印象深刻的，如一个2400磅230磅的弹性模量，拉伸强度和伸长率超过620％的高物理强度性能。 这种独特的粘合剂化合物的典型特性总结如下。 一个特殊的交联剂称为CRA 128可用于应用程序的长期耐水性得到最大限度的发挥。 建议增加2％的基础上乳胶的重量。 全粘接强度属性后覆膜。

Master Bond Polymer System LTX 128 is a newly developed fast drying high performance waterborne aliphatic polyester urethane laminating adhesive featuring a low activation temperature and excellent adhesive properties as well as remarkably high hot water immersion resistance. This low VOC C1.3%) polymer composition is furnished as a light tan milky liquid with a 38% solids content and a pH 8.0. It has a heat seal activation temperature of as low as 225°F (107°C). Adhesion to such diverse substrates as vinyl type polymers, polyesters, polyurethanes, low density polyethylenes as well as ABS and aluminum foils etc is outstanding. Master Bond Polymer System LTX128 has impressively high physical strength properties such as a tensile strength of 2400 psi a modulus of 230 psi and in excess of 620% elongation. Typical properties of this unique adhesive compound are summarized below. A special cross linking agent called CRA 128 is available for applications where long term water resistance has to be maximized. A recommended addition is 2% based on the weight of the latex. Full adhesive strength properties are developed after lamination.